| 分类 | 测试项目 | 检测标准 | 例图 |
|---|---|---|---|
|
压敏胶带 Sensitive Tape |
总厚度 Total Thickness |
ASTM D3652/D3652M；GB/T 7125；EN 1942 |
|
| 胶粘层厚度 Thickness of Adhesive |
ASTM D3652/D3652M；GB/T 7125 |
||
| 基材厚度Thickness of Liner |
ASTM D3652/D3652M；GB/T 7125 |
||
| 宽度Width | ASTM D5750/D5750M | ||
| 长度Length | ASTM D5750/D5750M | ||
| 解卷力Unwind Force |
ASTM D3811/D3811M；GB/T 4850；EN 1944 |
||
| 拉伸强度、伸长率 Tensile Strength and Elongation |
ASTM D3759/D3759MProcedure A、C、D；ASTM D1000；GB/T 30776 方法A；ISO 29864 method A；EN 14410 method A；JIS Z 0237 Section 8 |
||
| 初粘性((滚球法) Tack（rolling ball method） |
GB/T 4852方法A、B；JIS Z 0237 Section 14；PSTC-6 |
||
| 环形初粘性Loop tack |
GB/T 31125 方法A；ASTM D6195Method A |
||
| 180° 剥离强度 Peel Adhesion at 180° |
ASTM D3330/D3330M Method A,B,C,D,E ；ISO 29862Method 1,2,3,4；BS EN 1939Method 1,2,3,4；GB/T 2792方法1,2,3,4；JIS Z 0237Section 10Method 1,2,3,4；PSTC-101Method A |
||
| 低温180°剥离强度 180° Peel Adhesion at low temperature |
ISO 29862Method 1,2,3,4；BS EN 1939Method 1,2,3,4；GB/T 2792方法1,2,3,4 |
||
| 90°剥离强度 Peel Adhesion at 90° |
ASTM D3330/D3330M Method F；ASTM D6252/D6252M；JIS Z 0237Section 10.4.6；GJB 446；ISO 29862附录B；BS EN 1939附录B；GB/T 2792附录B |
||
| 垂直持粘性 Holding Power in vertical direction |
ASTM D3654/D3654M Procedure A；ASTM D3654/D3654M Procedure B；ASTM D3654/D3654M Procedure D ；ASTM D3654/D3654M Procedure H ；GB/T 4851 方法 A\B\C；ISO 29863 方法 A\B\C；EN 1943 方法 A\B\C；GB/T 4851方法G；ISO 29863 方法 A\B\C；EN 1943方法 A\B\C；PSTC-107Procedure B；JIS Z 0237第13节 |
||
| 水平持粘性 Holding Power in horizontal direction |
ASTM D3654/D3654M Procedure E ； ASTM D3654/D3654M Procedure F；GB/T 4851 方法 D\E\F；ISO 29863 方法 D\E\F；EN 1943 方法 D\E\F |
||
| 90º持粘性 Holding Power at 90ºangle |
ASTM D2860/D2860M | ||
| 耐冲击Impact resistance | AS/NZS 4275.3 | ||
| 耐水性Water resistance | ASTM D5570/D5570MMethod A | ||
| 水透过率 Water penetration rate |
ASTM D3816/D3816M | ||
| 水蒸气透过率 Water Vapor Transmission |
ASTM D3833/D3833M | ||
| 胶粘剂 Adhesive |
拉伸性能Tensile property | ASTM D897 | |
| 180° 剥离强度 (挠性材料对刚性材料) 180° Peeling Strength |
ASTM D903;EN ISO 8510-2;GB/T 2790 |
||
| 90°剥离强度 90 ° peel strength |
ASTM D6862 | ||
| 剥离强度 Peel strength |
ASTM C794 | ||
| T型剥离强度 (挠性材料对挠性材料) T Peeling Strength |
ASTM D1876;ISO 11339;GB/T 2791 |
||
| 剥离强度－浮辊法 Peeling Strength－Floating Roller Method |
ISO 4578GB/T 7122;BS EN 1464 |
||
| 不挥发物含量 Nonvolatile Content |
ASTM D1489;GB/T 2793 |
||
| 拉伸剪切强度 Tensile Lap-Shear Strength |
ASTM D1002;ISO 4587;GB/T 7124;BS EN 1465;ASTM D3163;EN 1373;ASTM D816 Method B |
||
| 低温拉伸剪切 Shear strength of adhesive by tension loading at low temperature |
GJB 1709 | ||
| 高温拉伸剪切 Strength properties of adhesives in shear loading at high temperature |
GJB 444 | ||
| 压缩剪切强度 Compression Shear Strength |
GB/T 17517;HG/T 2727 附录A |
||
| 拉伸粘结强度 Tensile Adhesive Strength |
GB/T 13477.8 | ||
| 劈裂强度 Cleavage Strength |
GB/T 7749 | ||
| 粘度Viscosity |
ASTM D3236;HG/T 3660方法B;GB/T 2794；GB/T 12010.2附录E;ASTM D1084Method B、C; SAE J243 Section 3.2.2;GB/T 22314 |
||
| 密度(重量杯法) Density（Method of weight cup） |
GB/T 13354- | ||
| pH值 pH value |
GB/T 14518 | ||
| 耐水性 Water resistance |
ASTM D5570/D5570M Method B | ||
| 胶粘剂制样 Preparation of adhesive specimen |
参考相关胶粘剂测试标准 | ||
| 涂料 Coating |
漆膜厚度 Coating thickness |
ISO 2178；GB/T 4956；ASTM D7091；ISO 2808Method 7C和7D；GB/T 13452.2方法7C和7D；ISO 2360；GB/T 4957；ASTM D4138；ASTM D6132；ISO 2808方法10；GB/T 13452.2 方法10 |
|
| 漆膜附着力 （划格法） Adhesion |
ASTM D3359Method A、B；ISO 16276-2；ISO 2409；GB/T 9286；AS/NZS 1580.408.4；JIS K5600-5-6 |
||
| 漆膜附着力 （划叉法） Adhesion |
JIS K5400Section 8.5.3 | ||
| 漆膜附着力 （画圈法） Adhesion |
GB/T 1720 | ||
| 漆膜附着力 （拉开法） Adhesion |
ASTM D4541Method C、E；ISO 4624 Clause 9.4.2；GB/T 5210 条款9.4.2 |
||
| 巴克霍尔兹压痕试验 Buchholz indentation test |
GB/T 9275；ISO 2815 |
||
| 铅笔硬度 Pencil hardness |
ASTM D3363；ISO 15184；BS EN ISO 15184； GB/T 6739；JIS K5600-5-4 |
||
| 漆膜耐冲击性 Impact strength |
ASTM D2794；ISO 6272-2；GB/T 20624.2；GB/T 1732；ISO 6272-1；GB/T 20624.1；JIS K5600-5-3 |
||
| 冲击测试 Falling weight test |
JIS K5600-5-3 Section 6 | ||
| TABER旋转耐磨性 Taber Rotary Abrasion |
ASTM D4060；ASTM D6037Method A；ASTM D3884；GB/T 1768；ISO 7784-1；ISO 7784-2；ASTM D7255；ASTM D3389；GB/T 18102 6.3.11节；ASTM C501；EN 438-2 Clause 11；GB/T 245086.5.15；ASTM C1353/C1353M；ISO 5470-1；ISO 15372 Clause 6.2.15；ASTM F1478 |
||
| 线性磨耗 linear abrasion |
GB/T 23989；ISO 105 X12；GB/T 3920；AATCC 8；ISO 20433；JIS L0849；SAE J861；ISO 11640；QB/T 2537 |
||
| 耐磨 Resistance to Abrasion |
SAE J948 | ||
| TABER线性磨耗 TABER Linear Abrasion |
GMW 14125；SAE J2027 Section 5.2.3 |
||
| 落砂磨耗 Falling sand abrasion |
ASTM D968Method A；GB/T 8013.1 附录A；GB/T 12967.7；GB/T 23988 |
||
| 落砂磨耗 Falling sand abrasion |
GMW 15487；GMW14671 Section 3.9.4 |
||
| RCA磨耗RCA abrasion | ASTM F2357 | ||
| 漆膜耐柔韧性 Flexibility |
ISO 1519；GB/T 6742；GB/T 1731；ASTM D522/D522MMethod A；ISO 6860；GB/T 11185；ASTM D4145 |
||
| 耐刮擦测试 Scratch test |
ISO 1518-1；GB/T 9279.1；EN 438-2 Clause 25；BS EN 15186 |
||
| 耐磨 Mar resistance |
ASTM D5178；ASTM D2197；ISO 12137；JIS K5600-5-5；ASTM D6279 |
||
| 植绒耐磨 Flocked Abrasion Resistance |
PV 3932 |
||
| ABREX® 多功能手指磨耗仪 manual abrasion test |
GB/T 2423.53；IEC 60068-2-70 |
||
| 耐码垛性试验 Pressure test for stackability |
GB/T 9280 | ||
| 耐污染测试 Contamination resistance |
MS210 | ||
| 杯突 Cupping test |
ISO 1520；GB/T 9753；JIS K 5600-5-2；GB/T13448 Section 14.5.1；GB/T13448 Section 14.5.2 |
||
| 涂层耐洗刷性 Brush resistance |
ISO 11998；GB/T 9266；GMW14865；STD 1024,7134；ASTM D2486 |
||
| 碎石冲击 Stone Chip test |
SAE J400；ASTM D3170/D3170M；DIN EN ISO 20567-1；BS EN ISO 20567-1 |
||
| 密度 Density |
ASTM D1475；ISO 2811-1GB/T 6750 |
||
| 粘度 Viscosity |
ASTM D2196Method A；GB/T 1723（涂-1/涂-4粘度计）甲法、乙法；GB/T 2794（旋转粘度计法）；GB/T 7193（旋转粘度计法）；ASTM D5125-(ISO流量杯法）；ASTM D562-斯脱默粘度计）；ISO 2431（ISO 流量杯法）；GB/T 9269 B法(斯脱默粘度计)；GB/T 6753.4（ISO 流量杯法）；ASTM D3236（旋转粘度计法）；ASTM D1200（福特杯） |
||
| 细度Fine degree |
GB/T 1724；ISO 1524；GB/T 6753.1 |
||
| 稠度Consistency | GB/T 1749 | ||
| 干燥时间 Dry time |
ISO 9117-3；GB 9273；GB/T 1728；GB/T 6753.2；ISO 9117-4 Method A；ASTM D5895Method A |
||
| 镜面反射率和镜面光泽度 Specular reflectance and specular gloss |
ISO 7668 Method A、Method C、Method D；GB/T 20503方法A、方法C、方法D |
||
| 光反射系数 luminous reflectance factor |
ASTM E1477 | ||
| 反射率 Light reflectance value |
BS 8493:2008+A1 | ||
| 漆膜光泽度 Gloss of Coating Film |
ASTM D523；ISO 2813；GB/T 9754； JIS K5600-4-7；GB/T 13891；EN 13523-2 |
||
| 色差 Color Differences |
ASTM D2244；GB/T 11186.1,2,3；GB/T 3979；AATCC 173；BS EN ISO 105 J03；ISO 105-J03；GB/T 3810.16；ISO 10545-16；ISO 105-A02/Cor 2；EN 20105-A02；AATCC Evaluation Procedure 1；GB/T 250；ASTM D2616； DIN EN ISO 11664-3；PV 3952；QB/T 2804；TAPPI T 524 OM；TAPPI T 562 OM；TAPPI T 646 OM；ASTM E1347；GB/T 7921；EN 13523-3；ASTM E1331 |
||
| 多角度色差 Multi-Angle Color Difference |
SAE J1545；ES-X63131Clause 5.6.2； ASTM D2244；ASTM E116；ASTM E308；DIN 6175-2 |
||
| 黄色指数Yellow Index | ASTM E313 | ||
| 桔皮(LW, SW, du, Wa, Wb, Wc, Wd, We, DOI)Orange peeling | NES M0141第6.1.8节 | ||
| 双波扫描(LW、SW、Du、Wa、Wb、Wc、Wd、We) Dual Wave Scan |
PSA D25 5540 | ||
| WS值Wave Scan Value | ES-X63131 第5.8节 | ||
| CF值CF Value | MTS-F03-03-002-B1第4.19节 | ||
| 涂料遮盖力 Hiding Power of Paint |
ISO 2814；GB/T1726（甲法：刷涂法）；ISO 6504-3 |
||
| 漆膜耐水性(浸泡法) Water resistance (immersion method) |
ASTM D870；ISO 2812-2；GB/T 5209； GB/T 1733；JIS K5600-6-2 |
||
| 漆膜耐化学试剂性 Reagent resistance |
ISO 2812-1；GB 9274 方法1；GB 9274 方法2；GB 9274-方法3；GB/T 9265；EN 12720,AMD.1；EN 12721,AMD.1 |
||
| 漆膜耐溶剂性 Solvent resistance |
ASTM D5402；GB/T 23989Method A；ASTM D4752 |
||
| 漆膜耐化学试剂 Resistance to liquids（Spotting methods） |
ISO 2812-4 | ||
| 漆膜耐化学试剂（吸附介质法） resistance to liquids（Method using an absorbent medium） |
ISO 2812-3 | ||
| 耐盐浴 Resistance to salt bath |
QB/T 1950 | ||
| 耐人工汗液 Synthetic perspiration resistance |
BS EN ISO 12870Clause 8.3； ISO 3160-2Clause 7.4 |
||
| 耐水性 Resistantance to water |
GB/T 1733 | ||
| 硝酸蒸汽腐蚀 Nitric acid vapour test |
ISO 14647；EIA 364-53B |
||
| 耐腐蚀 Corrosion resistance |
ASTM B380 | ||
| 丝状腐蚀 Filiform corrosion |
ISO 4623-；GB/T 26323；GB/T 13452.4；ISO 4623-1 |
||
| 针孔腐蚀 Pitting corrosion |
ISO 8993 | ||
| 改进腐蚀试验 Modified corrodkote corrosion test |
DIN 50958 | ||
| 耐高温 Heat resistant properties |
ASTM D2485 Method A | ||
| 抗粘连接 Blocking Resistance |
ASTM D4946 | ||
| 烘烤质量损失 Mass loss by baking |
ISO 8130-7；GB/T 21782.7 |
||
| 固体含量 Solid content |
ISO 3251；GB/T 1725；GB/T 1747.2；ASTM D4441 |
||
| 不挥发份含量 Non volatile matter |
ASTM D1353 | ||
| 挥发份含量 Volatile content |
ASTM D2369；ISO 787-2 |
||
| 不挥发物体积分数 Volume of Non-volatile Matter |
GB/T 9272；ISO 3233, MOD |
||
| 白垩试验 Chalking Test |
ASTM D4214-Method B | ||
| 镀层厚度 Thickness of Plating |
ASTM B 504；GB/T 495；ISO 2177；DIN EN ISO 2177；DIN 50022；ASTM B764；GB/T 16921；ISO 3497；DIN EN ISO 3497；ASTM B568；ASTM A754/A754M；JIS H8501 |
||
| 铬孔密度 Micropore Density of Chrome-Plated Surfaces |
PV 1063；GS 97017 Section 5.2.3 |
||
| 微孔数和微裂纹测试 Minimum Discontinuities |
ASTM B604Annex X4 |
||
| 微裂纹Microcracks | DIN 53100 | ||
| 液体涂料制板 Coating plate preparation with liquid coating |
空气喷涂 |